4004 TAMİRART S40

High-Strength Structural Repairing Mortar
TECHNICAL DATA SHEET

Definition
Sulphate and chloride resistant, cement based thixotropic structural repair mortar having polymer and fiber addition.
Usage Areas
Repairing damaged high strength concrete, Protection of concrete against sulphates and chlorides, Repairing underwater and substructural concrete members, Repairing tie-rod holes on concrete structure, Repairing concrete structures which is subject to sea water, Repairing 5-40 mm thick per coat
Package
25 kg multi-ply paper bags.

Features
High adhesion strength. High compression strength. Resistant to freeze thaw cycle. Resistant to sulphates and chlorides Resistant to water. Adjustable viscosity. Suitable for vertical and overhead application. Non-corrosive.


Technical Properties
 (at 23°C and 50% RH)
General Data
Appearance: Grey powder
Shelf Life: 12 months when stored in the original sealed packing in dry place
Application Data
Application Temperature Range: (+5°C)-(+35°C)
Mixing Ratio: 2.5-3.5 liters water / 25 kg powder
Pot Life: 1 hour
Ready For Use: 24 hours
Consumption (avr.): 20 kg/m² (per 10 mm thickness)
Application Thickness: Min. 5 mm-Max. 40 mm
Performance Data
Flexural Strength (EN 12190): ≥ 3.0 N/mm² (1 day), ≥ 5.0 N/mm² (7 days), ≥ 7.0 N/mm² (28 days)
Compressive Strength (EN 12190): ≥ 20.0 N/mm² (1 day), ≥ 40.0 N/mm² (7 days), ≥ 55 N/mm² (28 days)
Modulus of Elasticity (EN 13412): ≥ 20000 N/mm²
Bonding to Concrete (EN 1542): ≥ 2.0 N/mm²
Capillary Water Absorption (EN 13057): ≤ 0.5 kg/m²h0.5
Service Temperature Range: (-30°C)-(+80°C)
Restrained Shrinkage-Expansion (EN 12617-4): ≥ 2.0 N/mm²
Dangerous Substances: See SDS.
Reaction to Fire (EN 13501-1): A1